magnesium plate
WE43 WE54 WE94 AZ91D AZ31B AZ40M AZ41 AZ61 AZ80 AZ90
AZ31B is a wrought magnesium base alloy with good room-temperature
strength and ductility combined with corrosion resistance and
weldability. Increased strength is obtained by strain hardening
with a subsequent partial anneal (H24 and H26 tempers). Our sheet
and plate's size range is:
Sheet: thickness from 1mm to 6mm; Max. width is 600mm; Max. length
is 6000mm;
Plate: thickness from 6 mm to 200mm; Max. width is 2000mm; Max.
length is 6000mm;
Block: We can supply cut-to-size blocks according to customer's
requirements.
Coil: thickness from 0.5 to 2.7mm, max. width 240mm;
Applications
Sheet and plate in AZ31B find application in medium strength
service at temperatures below 150°C. Diverse uses including
aerospace, aircraft, concrete tools, 3C (cell phone / camera /
computer), speaker cones and textile machinery can all benefit from
light weight AZ31B.
AZ31B is non-magnetic and has high electrical and thermal
conductivity filling the requirements for RFI and EMI shielding in
the electronics and computer industries.
Superplastic forming of AZ31B sheet at elevated temperatures allows
production of a wide variety of intricate parts for automotive
uses. Monocoque construction utilizing formed sheet can be adapted
to many commercial applications.
SPECIFICATIONS
ASTM B90/B90M-07
AMS 4375
AMS 4376
AMS 4377
CHEMICAL COMPOSITION
Al: 2.5-3.5%
Zn: 0.7-1.3%
Mn: 0.20 – 1.0%
Mg: Balance
PHYSICAL PROPERTIES
Density: 1.78
Coefficient of thermal expansion: 26.8 x 10-6K-1
Specific heat: 1040 Jkg-1k-1
Thermal conductivity: 76.9Wm-1k-1
Electrical resistivity: 92nΩm
Modulus of elasticity: 45 x 109Pa
Poissons ratio: 0.35
Melting range: 566 - 632°C
HEAT TREATMENT
No thermal treatment is available for increasing the strength of
this alloy after fabrication.
MECHANICAL PROPERTIES
Alloy and Temper | Thickness (mm) | Yield Strength 0.2% offset (MPa) | Tensile strength (MPa) | Elongation In 5.65 √A (%) |
AZ31B-O | 0.5 – 1.5 | 125 | 221 | 10 |
1.5 – 6.3 | 105 | 221 | 9 |
6.3 - 75 | 105 | 221 | 8 |
AZ31B-H24 | 0.5 – 6.3 | 200 | 269 | 5 |
6.3 -9.5 | 179 | 262 | 7 |
9.5 – 12.7 | 165 | 255 | 8 |
12.7 - 25 | 152 | 248 | 8 |
25- 50 | 138 | 234 | 6 |
50 - 80 | 124 | 234 | 7 |
AZ31B-H26 | 6.3 - 10 | 186 | 269 | 6 |
10 – 12.5 | 179 | 262 | 6 |
12.5 - 20 | 172 | 255 | 5 |
20 – 25 | 159 | 255 | 5 |
25 - 40 | 152 | 241 | 5 |
40 - 50 | 148 | 241 | 5 |
The sheet and plate shall conform to the tensile requirements in
above Table unless other agreement is made between seller and
purchaser. Mechanical Properties for sizes and tempers not shown in
above Table shall be as agreed upon by seller and purchaser.
OTHER PROPERTIES
Typical Hadness
O temper: 67 Rockwell E
H24 temper: 83 Rockwell E
WELDABILITY
Excellent weldability with gas shielded arc using AZ61A (preferred)
or AZ92A filler rod; post weld stress relief is required to prevent
stress corrosion cracking. Resistance welding is excellent.
MACHINING
AZ31B, like all magnesium alloy sheet and plate, machines faster
than any other metal. Providing the geometry of the part allows,
the limiting factor is the power and speed of the machine rather
than the quality of the tool material. The power required per cubic
centimeter of metal removed varies from 9 to 14 watts per minute
depending on machining operation.
DENT RESISTANCE
Weight for weight, AZ31B-H24 has proven to be superior to
competitive materials in its resistance to denting at moderate
energy levels.
Dent Resistance of 1mm Gauge Sheet (Dent depth in mm from 25mm
spherical redius indentor on 350mm span)
| Impact Energy 0.34 J | Impact Energy 0.62 J | Impact Energy 1.25 J |
AZ21B-H24 6061 – T6 3003 – H14 5052 – H34 2024 – T6 SAE 1010 Mild Steel | 0.66 0.94 2.24 1.55 0.99 1.09 | 1.42 1.52 3.23 2.41 1.52 1.70 | 2.34 2.46 4.90 3.35 2.29 2.67 |
SURFACE TREATMENT
All the normal chromating, anodizing, plating, and finishing
treatment are readily applicable. AZ31B also responds well to
plasma electrolytic oxidation finishing.